Standard Alloys

Leaded Tin Bronze Alloys

Leaded Red Brass Alloys

  • C83600
  • C83800
  • C84200
  • C84400
  • C84800
  • C85700

Manganese Bronze Alloys

  • C86200
  • C86300
  • C86500

Aluminum Bronze Alloys

  • C95200
  • C95300
  • C95300HT
  • C95400
  • C95400HT
  • C95410
  • C95410HT
  • C95500
  • C95500HT
  • C95510HT
  • C95520HT
  • C95800
  • C95900

High Tin Bronze Alloys

  • C90300
  • C90500
  • C90700
  • C90800
  • C90810
  • C91000
  • C91100
  • C91300
  • C91600
  • C91700

High Lead Tin Bronze

  • C93400
  • C93500
  • C93600
  • C93700
  • C93800
  • C93900
  • C94000
  • C94100
  • C94300
  • Bronze Family: Leaded Tin Bronze
  • Solids: 1/2" to 13" OD
  • Tubes: 1" to 16" OD
  • Rectangles: Up to 20"
  • Standard Lengths: 144"

Typical Uses

  • Automotive Automotive Fittings
  • Fasteners Washers
  • Industrial Thrust Washers, Pumps, Bushings, Machine Parts, Main Spindle Bearings, Machine Tool Bearings, Bearings for Cranes, Trunnion Bearings, Roll Neck Bearings, Rolling Mill Bearings, Linkage Bushings for Presses, Fuel Pump Bushings, Water Pump Bushings, Diesel Engine Wrist Pin Bushings, Forging Press Toggle Lever Bearings, Hydraulic Press Stuffing Box, Hydraulic Press Main Lining, Pump Impellers, General Purpose Bushings, Fittings, Pump Fixtures, Insert Bearings, Bearings

Similar or Equivalent Specification

CDA ASTM ASARCON SAE AMS Federal Ingot# Military Other Desc
C93200 B505 77 660   QQ-C-390 B TYPE III 315 MIL-B-11553 COMP. 12  
      J461          
      J462          

Chemical Composition (according to ASTM B505-08)

Cu% Sn% Pb% Zn% Fe% Ni% Sb% P% S% Al% Mn% Si%
Note: Single values represent maximums.
  • † In determining copper minimum, copper may be calculated as copper plus nickel.
81.00-85.00 6.30-7.50 6.00-8.00 2.00-4.00 0.20 1.00† 0.35 1.5 0.08 0.005 N/A 0.005

Mechanical Properties (according to ASTM B505-08)

Tensile Strength (min) Yield Strength (at .5% extention under load min) Elongation (in 2in. or 50mm min, %) Brinell Hardness (min) Remarks
Ksi MPa Ksi MPa
35 241 20 138 10    

Machinability

Alloy Rating Density
C93200 70 0.322

Physical Properties (provided by CDA)

US Customary Metric
Melting Point - Liquidus 1790 F 977 C
Melting Point - Solidus 1570 F 854 C
Density 0.322 lb/in3 at 68 F 8.91 gm/cm3 @ 20 C
Specific Gravity 8.910 8.91
Electrical Resistivity 85.90 ohms-cmil/ft @ 68 F 14.29 microhm-cm @ 20 C
Electrical Conductivity 12 %IACS @ 68 F 0.07 MegaSiemens/cm @ 20 C
Thermal Conductivity 33.60 Btu · ft/(hr · ft2·°F)at 68F 58.2 W/m · °K at 20 C
Coefficient of Thermal Expansion 10 ·10-6 per oF (68-392 F) 18.0 ·10-6 per °C (20-200 C)
Specific Heat Capacity 0.090 Btu/lb/°F at 68 F 377.1 J/kg · °K at 293 K
Modulas of Elasticity in Tension 14500 ksi 100000 MPa

Fabrication Properties (provided by CDA)

Joining Technique Suitability
Soldering Excellent
Brazing Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Not Recommended
Coated Metal Arc Welding Not Recommended

Thermal Properties (provided by CDA)

Treatment Temp./Time - US Temp./Time - SI
Stress Temperature 500 260
Solution Minimum    
Solution Maximum    
Solution Time 0.0
Solution Medium None
Precipitation Value    
Precipitation Time    
Precipitation Medium None
Annealing Minimum    
Annealing Maximum    
Annealing Time
Hot Works Minimum    
Hot Works Maximum    
   

See what an honest, hard-working metal distributor can do for you.
Call or email us today.

BEARTECH ALLOYS, Inc.
(877) 232-7832 Toll Free
(714) 550-1700 * (714) 550-1710 Fax
910 S. Placentia Ave, Suite A
Placentia, CA 92870