- Bronze Family: High Tin Bronze
- Solids: 1/2" to 10" OD
- Tubes: 1" to 16" OD
- Rectangles: Up to 20"
- Standard Lengths: 144"
- Industrial Restaurant Equipment, Worm Wheels, Gears, Bearings for Heavy Loads and Relatively Low Speeds, Bearings, Gear Boxes, Speed Reducers, Valve Bodies, Worm Gears
| CDA |
ASTM |
ASARCON |
SAE |
AMS |
Federal |
Ingot# |
Military |
Other Desc |
| C90700 |
ASTM B505 |
110 |
SAE 65 |
|
QQ-C-390B TYPE III |
205 |
|
HIGH TIN BRONZE, 65 |
| |
|
|
SAE J461 |
|
|
|
|
|
| |
|
|
SAE J462 |
|
|
|
|
|
| Cu% |
Sn% |
Pb% |
Zn% |
Fe% |
Ni% |
Sb% |
P% |
S% |
Al% |
Mn% |
Si% |
Note: Single values represent maximums.
- A In determining copper minimum, copper may be calculated as copper plus nickel.
|
| 88.00-90.00 |
10.00-12.00 |
0.50 |
0.50 |
0.15 |
0.50A |
0.20 |
1.5 |
0.05 |
0.005 |
N/A |
0.005 |
| Tensile Strength (min) |
Yield Strength (at .5% extention under load min) |
Elongation (in 2in. or 50mm min, %) |
Brinell Hardness (min) |
Remarks |
| Ksi |
MPa |
Ksi |
MPa |
|
|
|
| 40 |
276 |
25 |
172 |
10 |
N/A |
|
| Alloy |
Rating |
Density |
| C90700 |
20 |
0.317 |
| |
US Customary |
Metric |
| Melting Point - Liquidus |
1830 F |
999 C |
| Melting Point - Solidus |
1528 F |
831 C |
| Density |
0.317 lb/in3 at 68 F |
8.77 gm/cm3 @ 20 C |
| Specific Gravity |
8.770 |
8.77 |
| Electrical Resistivity |
107.40 ohms-cmil/ft @ 68 F |
17.86 microhm-cm @ 20 C |
| Electrical Conductivity |
10 %IACS @ 68 F |
0.056 MegaSiemens/cm @ 20 C |
| Thermal Conductivity |
40.80 Btu · ft/(hr · ft2·°F)at 68F |
70.6 W/m · °K at 20 C |
| Coefficient of Thermal Expansion |
10.20 ·10-6 per oF (68-392 F) |
18.4 ·10-6 per °C (20-200 C) |
| Specific Heat Capacity |
0.090 Btu/lb/°F at 68 F |
377.1 J/kg · °K at 293 K |
| Modulas of Elasticity in Tension |
15000 ksi |
103400 MPa |
| Magnetic Permeability |
1 |
1.0 |
| Joining Technique |
Suitability |
| Soldering |
Excellent |
| Brazing |
Good |
| Oxyacetylene Welding |
Fair |
| Gas Shielded Arc Welding |
Fair |
| Coated Metal Arc Welding |
Fair |
| Treatment |
Temp./Time - US |
Temp./Time - SI |
| Stress Temperature |
500 |
260 |
| Solution Minimum |
|
|
| Solution Maximum |
|
|
| Solution Time |
0.0 |
| Solution Medium |
None |
| Precipitation Value |
|
|
| Precipitation Time |
|
|
| Precipitation Medium |
None |
| Annealing Minimum |
|
|
| Annealing Maximum |
|
|
| Annealing Time |
|
| Hot Works Minimum |
|
|
| Hot Works Maximum |
|
|
|