Leaded Tin Bronze Alloys - C92200

Standard Alloys

Leaded Tin Bronze Alloys

Leaded Red Brass Alloys

  • C83600
  • C83800
  • C84200
  • C84400
  • C84800
  • C85700

Manganese Bronze Alloys

  • C86200
  • C86300
  • C86500

Aluminum Bronze Alloys

  • C95200
  • C95300
  • C95300HT
  • C95400
  • C95400HT
  • C95410
  • C95410HT
  • C95500
  • C95500HT
  • C95510HT
  • C95520HT
  • C95800
  • C95900

High Tin Bronze Alloys

  • C90300
  • C90500
  • C90700
  • C90800
  • C90810
  • C91000
  • C91100
  • C91300
  • C91600
  • C91700

High Lead Tin Bronze

  • C93400
  • C93500
  • C93600
  • C93700
  • C93800
  • C93900
  • C94000
  • C94100
  • C94300
  • Bronze Family: Leaded Tin Bronze
  • Solids: 1/2" to 13" OD
  • Tubes: 1" to 16" OD
  • Rectangles: Up to 20"
  • Standard Lengths: 144"

Typical Uses

  • Architecture Ornamental Castings
  • Building Heating Equipment, Cooling Equipment
  • Fasteners Nuts
  • Industrial Cryogenic Valves, Valves for Water Meters, Medium Pressure Hydraulic Equipment, Valve Components, Pumps Used to 550 F, Pump Impellers, Fittings Used to 550 F, Gears, Piston Rings, Bushings, Bearings
  • Marine Marine Castings
  • Plumbing Medium Pressure Steam Equipment to 550 F

Similar or Equivalent Specification

CDA ASTM ASARCON SAE AMS Federal Ingot# Military Other Desc
C92200 ASTM B505 190 SAE J461   QQ-C-390B TYPE III 245 MIL-B-11553 COMP. 1 NAVY "M" STEAM BRONZE
  ASTM B62   SAE J462   QQ-B-1005 COMP. 1      

Chemical Composition (according to ASTM B505-08)

Cu% Sn% Pb% Zn% Fe% Ni% Sb% P% S% Al% Mn% Si%
Note: Single values represent maximums.
  • A In determining copper minimum, copper may be calculated as copper plus nickel.
86.00-90.00 5.50-6.50 1.00-2.00 3.00-5.00 0.25 1.0A 0.25 1.5 0.05 0.005 N/A 0.005

Mechanical Properties (according to ASTM B505-08)

Tensile Strength (min) Yield Strength (at .5% extention under load min) Elongation (in 2in. or 50mm min, %) Brinell Hardness (min) Remarks
Ksi MPa Ksi MPa
38 262 19 19 18 N/A  

Machinability

Alloy Rating Density
C92200 42 0.312

Physical Properties (provided by CDA)

US Customary Metric
Melting Point - Liquidus 1810 F 988 C
Melting Point - Solidus 1518 F 826 C
Incipient Melting 600 F 315 C
Density 0.312 lb/in3 at 68 F 8.64 gm/cm3 @ 20 C
Specific Gravity 8.640 8.64
Electrical Resistivity 72.50 ohms-cmil/ft @ 68 F 12.0 microhm-cm @ 20 C
Electrical Conductivity 14 %IACS @ 68 F 0.083 MegaSiemens/cm @ 20 C
Thermal Conductivity 40.20 Btu · ft/(hr · ft2·°F)at 68F 69.6 W/m · °K at 20 C
Coefficient of Thermal Expansion 10 ·10-6 per oF (68-392 F) 18.0 ·10-6 per °C (20-200 C)
Specific Heat Capacity 0.090 Btu/lb/°F at 68 F 377.1 J/kg · °K at 293 K
Modulas of Elasticity in Tension 14000 ksi 96500 MPa
Magnetic Permeability 1 1.0

Fabrication Properties (provided by CDA)

Joining Technique Suitability
Soldering Excellent
Brazing Excellent
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Not Recommended
Coated Metal Arc Welding Not Recommended

Thermal Properties (provided by CDA)

Treatment Temp./Time - US Temp./Time - SI
Stress Temperature 500 260
Solution Minimum    
Solution Maximum    
Solution Time 0.0
Solution Medium None
Precipitation Value    
Precipitation Time    
Precipitation Medium None
Annealing Minimum    
Annealing Maximum    
Annealing Time
Hot Works Minimum    
Hot Works Maximum    
   

See what an honest, hard-working metal distributor can do for you.
Call or email us today.

BEARTECH ALLOYS, Inc.
(877) 232-7832 Toll Free
(714) 550-1700 * (714) 550-1710 Fax
910 S. Placentia Ave, Suite A
Placentia, CA 92870