SPECIFICATION DATA SHEET: High Silicon Bronze C-65510 Stainless Steel

BAR TUBE PIPE
PSQ SHAFT   WELDING ROD CASTINGS
FORGINGS   PLATE   FLANGES
TG&P SHAFTS SHEET FITTINGS

Chemical Composition
(%max., unless shown as range or min.)
  Cu(1) Fe Pb Mn Ni(2) Si Zn
Min./Max. Rem. .8 .05 .50-1.3 .6 2.8-3.8 1.5
Nominal 97.0 - - .9 - 3.0 -

(1) Cu value includes Ag.
(2) Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.

Applicable Specifications
Product Specification
Bar SAE J461, J463
Bar, Forging ASTM B124
Bar, Rolled ASME SB98
ASTM B96, B98
SAE J461, J463
Bar, Rolled, Pressure Vessels ASME SB96
ASTM B96
Bolts ASTM F468
Forgings, Die ASTM B283
Nuts ASTM F467
Pipe ASME SB315
ASTM B315
Plate ASME SB96
ASTM B96
Plate, Bridge and Bearing ASTM B100
Plate, Clad ASTM B432
Plate, Pressure Vessels ASME SB96
ASTM B96
Rod ASME SB98
ASTM B98
SAE J461, J463
Rod, Forging ASTM B124
Screws ASTM F468
Shapes ASME SB98
ASTM B98
SAE J461, J463
Shapes, Forging ASTM B124
Sheet ASME SB96
ASTM B96
SAE J461, J463
Sheet, Bridge and Bearing ASTM B100
Sheet, Pressure Vessels ASME SB96
ASTM B96
Strip ASME SB96
ASTM B96
SAE J461, J463
Studs ASTM F468
Tube ASME SB315
ASTM B315
MILITARY MIL-T-8231
Wire ASTM B105, B99

 

Common Fabrication Processes
Blanking, Drawing, Forming and Bending, Heading and Upsetting, Hot Forging and Pressing, Roll Threading and Knurling, Shearing, Squeezing and Swaging

 

Fabrication Properties
Joining Technique Suitability
Soldering Good
Brazing Excellent
Oxyacetylene Welding Good
Gas Shielded Arc Welding Excellent
Coated Metal Arc Welding Fair
Spot Weld Excellent
Seam Weld Excellent
Butt Weld Excellent
Capacity for Being Cold Worked Excellent
Capacity for Being Hot Formed Excellent
Forgeability Rating 40
Machinability Rating 30
Mechanical Properties
Mechanical Properties (measured at room temperature, 68 F (20 C)

*Fatigue Strength: 100 x 10 6cycles, unless indicated as [N]X 106.
Temper Section
Size		 Cold
Work		 Typ/
Min		 Temp Tensile
Strength		 Yield
Strength
(0.5% ext.
under load)		 Yield
Strength
(0.2%
offset)		 Yield
Strength
(0.05%
offset)		 El Rockwell
Hardness		 Vickens
Hard.		 Brinell
Hard.		 Shear
Strength		 Fatigue
Strength*		 Izod
Impact
Strength

in. %
F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb

mm.

C MPa MPa MPa MPa







MPa MPa J
Flat Products
H01 0.04 0 TYP 68 68 35 - - 30 75 - - 67 - - - 47 - 0.0

1

20 469 241 - - 30 75 - - 67 - - - 324 - 0.0
H02 0.04 0 TYP 68 78 45 - - 17 87 - - 75 - - - 50 - 0.0

1

20 538 310 - - 17 87 - - 75 - - - 345 - 0.0
H04 0.04 0 TYP 68 94 58 - - 8 93 - - 78 - - - 57 - 0.0

1

20 648 400 - - 8 93 - - 78 - - - 393 - 0.0
H06 0.04 0 TYP 68 104 60 - - 6 96 - - 80 - - - 60 - 0.0

1

20 717 414 - - 6 96 - - 80 - - - 414 - 0.0
H08 0.04 0 TYP 68 110 62 - - 4 97 - - 81 - - - 63 - 0.0

1

20 758 427 - - 4 97 - - 81 - - - 434 - 0.0
OS015 0.04 0 TYP 68 63 30 - - 55 66 - 90 - - - - 45 - 0.0

1

20 434 207 - - 55 66 - 90 - - - - 310 - 0.0
OS035 0.04 0 TYP 68 60 25 - - 60 62 - 85 - - - - 43 - 0.0

1

20 414 172 - - 60 62 - 85 - - - - 296 - 0.0
OS070 0.04 0 TYP 68 56 21 - - 63 40 - 76 - - - - 42 - 0.0

1

20 386 145 - - 63 40 - 76 - - - - 290 - 0.0
Rod
H02 1 20 TYP 68 78 45 - - 35 85 - - - - - - 52 - 0.0

25.4

20 538 310 - - 35 85 - - - - - - 359 - 0.0
H04 1 36 TYP 68 92 55 - - 22 90 - - - - - - 58 - 0.0

25.4

20 634 379 - - 22 90 - - - - - - 400 - 0.0
H06 1 50 TYP 68 108 60 - - 13 95 - - - - - - 62 - 0.0

25.4

20 745 414 - - 13 95 - - - - - - 427 - 0.0
OS050 1 0 TYP 68 58 22 - - 60 60 - - - - - - 43 - 0.0

25.4

20 400 152 - - 60 60 - - - - - - 296 - 0.0
Tube
H80 0.065 35 TYP 68 93 - - - 22 92 - - 78 - - - - - 0.0

1.7

20 641 - - - 22 92 - - 78 - - - - - 0.0
OS050 0.065 0 TYP 68 57 - - - 70 45 - - - - - - - - 0.0

1.7

20 393 - - - 70 45 - - - - - - - - 0.0
Wire
H00 0.08 0 TYP 68 70 40 - - 35 - - - - - - - 48 - 0.0

2

20 483 276 - - 35 - - - - - - - 331 - 0.0
H01 0.08 0 TYP 68 80 48 - - 20 - - - - - - - 52 - 0.0

2

20 552 331 - - 20 - - - - - - - 359 - 0.0
H02 0.08 0 TYP 68 98